"Rare" carbon fabrics
Epoxy system R2260 / H2266 for translucent laminates
Mixed price: 23.65 EUR / kg (each kilo includes 0.72 kg resin + 0.28 kg hardener)
(Price for quantities of 6-15 kg)
2260 epoxy system is specially formulated for the manufacturing of wind-surf boards and surf boards. It is adapted for hand lay up of carbon, aramid, glass and HMP fabrics and is compatible with all commercial foams: polystyrenes, polyurethanes, cross- linked and linear PVC foams.
Very good UV stability
Hardening without tack
Transparency of laminates
R2260 resin characteristics:
Very tough epoxy resin with high thermo-mechanical performance. Recommended for high performance wave and slalom wind surf boards and sandwich (or not sandwich for wave riding surf) construction.
Creates ultra light composite parts with high mechanical resistance and UV stability.
For surface preparation / plug finishing, high-gloss requirements.
Other applications: Jewellery, coating of coloured patterns, prototypes.
Instructions for application:
Work in a clean environment with heating facility.
Working temperature: 20 oC minimum, 35-40 oC maximum.
Maintain a constant temperature during lamination.
Avoid high ambient humidity (< 70%).
Avoid exposure to UV during cure. Laminates and coatings have a polymerization cycle of 14 days at 25 oC. Post curing offers greater UV resistance.
Do not wet sand laminates or coatings before 4 days at 25 oC.
Do not dilute with acetone, ester or alcohol based solvents.
Keep packaging well sealed as hardener is sensitive to carbonic gas and humidity.
A polyurethane paint finish can be applied without primer after sanding the final layer of resin.
Wait before post-curing: 24 hours
Minimum cure: 12 hours 40 oC
Optimum cure: 8 hours 60 oC
Physical properties of R2260 epoxy resin:
Appearance / colour: Light purple liquid
Viscosity (mPa.s) at 20 oC: 2000 (+-400)
Density (g/cm3) at 20 oC: 1.17 (+-0.01)
Physical properties of H2266 hardener:
Appearance / colour: Water clear liquid
Viscosity (mPa.s) at 20 oC: 50 (+-10)
Density (g/cm3) at 20 oC: 0.960 (+-0.01)
Mix properties of R2260 / H2266 system:
Mix viscosities (mPa.s) at 20 oC: 540
Mixing ratio by weight: 100 g / 38 g
Mixing ratio by volume: 100 ml / 50 ml (2 / 1)
Reactivity of R2260 / H2266 system:
Gel time 150 g mix at 25 oC: 20'
Dry to touch on 500 microns film at 25 oC: 2 h
Thru-dry, sandable at 25 oC: 10 h
For detailed data sheet please contact.
Intrastat Number for this product: Epoxy: 39073000, Hardener: 38249098